Celstran® PA66-GF60-0101P10
聚酰胺66/6共聚物
Ticona
Technical Data
產品說明
Material code according to ISO 1043-1: PA66
Nylon 66/6 copolymer reinforced by 50 weight percent long glass fibers. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long.
Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly.
The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding.
Can be used for substituting die cast metal with the advantage of Weight reduction, no corrosion problems, no post treatment.
總體
材料狀態 • 已商用：當前有效
資料 1 • Technical Datasheet (English)
• Processing - Injection (English)
Search for UL Yellow Card • Ticona
• Celstran®
供貨地區 • 北美洲 • 歐洲
填料/增強材料 • 長玻璃纖維, 50% 填料按重量
性能特點 • 低翹曲性 • 高強度
• 剛性，高 • 耐低溫撞擊
用途 • 金屬置換
RoHS 合規性 • 聯系制造商
加工方法 • 注射成型
樹脂ID (ISO 1043) • PA66
物理性能 額定值 單位制 測試方法
密度 1.67g/cm³ ISO 1183
粘數 120cm³/g ISO 307
機械性能 額定值 單位制 測試方法
拉伸模量
-- 19500MPa ISO 527-2/1A/1
80°C 13000MPa ISO 527-2
拉伸應力
斷裂 280MPa ISO 527-2/1A/5
80°C 160MPa ISO 527-2
拉伸應變
斷裂 2.1% ISO 527-2/1A/5
斷裂, 80°C 2.8% ISO 527-2
彎曲模量 ISO 178
23°C 18000MPa
80°C 13000MPa
彎曲強度 ISO 178
23°C 450MPa
80°C 290MPa
沖擊性能 額定值 單位制 測試方法
簡支梁缺口沖擊強度 ISO 179/1eA
-30°C 40kJ/m²
23°C 44kJ/m²
1 / 3
Celstran® PA66-GF60-0101P10
聚酰胺66/6共聚物
Ticona
沖擊性能 額定值 單位制 測試方法
簡支梁缺口沖擊強度 ISO 179/1eU
-30°C 84kJ/m²
23°C 100kJ/m²
無缺口伊佐德沖擊強度 ISO 180/1U
-30°C 76kJ/m²
23°C 95kJ/m²
熱性能 額定值 單位制 測試方法
熱變形溫度
1.8 MPa, 未退火 235°C ISO 75-2/A
8.0 MPa, 未退火 220°C ISO 75-2/C
熔融溫度 3 240°C ISO 11357-3
備注
1 通過這些鏈接您能夠訪問供應商資料。我們盡量保證及時更新資料；不過您可以從供應商處了解最新資料。
2 一般屬性：這些不能被視為規格。
3 10°C/min
|