Celstran® PA66-GF40-02P11/15
聚酰胺66
Ticona ides.com/prospector
Technical Data
產(chǎn)品說明
Material code according to ISO 1043-1: PA66
Heat stabilized Nylon 66 reinforced by 40 weight percent long glass fibers. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long.
Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly.
The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding.
Can be used for substituting die cast metal with the advantage of Weight reduction, no corrosion problems, no post treatment.
總體
材料狀態(tài) • 已商用：當(dāng)前有效
資料 1 • Technical Datasheet (English)
• Processing - Injection (English)
Search for UL Yellow Card • Ticona
• Celstran®
供貨地區(qū) • 歐洲
填料/增強(qiáng)材料 • 長(zhǎng)玻璃纖維, 40% 填料按重量
添加劑 • 熱穩(wěn)定劑
性能特點(diǎn) • 低翹曲性 • 高強(qiáng)度 • 熱穩(wěn)定性
• 剛性，高 • 耐熱性，高
用途 • 金屬置換
RoHS 合規(guī)性 • 聯(lián)系制造商
加工方法 • 片材擠出成型 • 注射成型
樹脂ID (ISO 1043) • PA66
物理性能 額定值 單位制 測(cè)試方法
密度 1.46g/cm³ ISO 1183
粘數(shù) 140cm³/g ISO 307
機(jī)械性能 額定值 單位制 測(cè)試方法
拉伸模量
-- 13700MPa ISO 527-2/1A/1
80°C 9000MPa ISO 527-2
拉伸應(yīng)力
斷裂 180MPa ISO 527-2/1A/5
80°C 130MPa ISO 527-2
拉伸應(yīng)變
斷裂 1.5% ISO 527-2/1A/5
斷裂, 80°C 2.0% ISO 527-2
彎曲模量 ISO 178
23°C 12600MPa
80°C 8000MPa
彎曲強(qiáng)度 ISO 178
23°C 260MPa
80°C 250MPa
1 / 3
Celstran® PA66-GF40-02P11/15
聚酰胺66
Ticona
沖擊性能 額定值 單位制 測(cè)試方法
簡(jiǎn)支梁缺口沖擊強(qiáng)度 ISO 179/1eA
-30°C 23kJ/m²
23°C 23kJ/m²
簡(jiǎn)支梁缺口沖擊強(qiáng)度 ISO 179/1eU
-30°C 41kJ/m²
23°C 40kJ/m²
懸壁梁缺口沖擊強(qiáng)度 ISO 180/1A
-30°C 35kJ/m²
23°C 24kJ/m²
熱性能 額定值 單位制 測(cè)試方法
熱變形溫度
1.8 MPa, 未退火 255°C ISO 75-2/A
8.0 MPa, 未退火 240°C ISO 75-2/C
熔融溫度 3 261°C ISO 11357-3
注射 額定值 單位制
加工（熔體）溫度 300 到 315°C
模具溫度 90.0 到 120°C
注射說明
During the processing of CELSTRAN it is important to watch and
control melt shear, for excessive shear reduces fiber length and
mechanical performance as well.
Processing recommendation:
• Conventional 3 zone screw, screw diameter minimum 40 mm
• Design flow channels for low melt shear
• Back pressure and screw rotation to realize a continous plastification performance and thus a homogeneous melt.
• Apply higher temperature settings than for short fiber compounds
備注
1 通過這些鏈接您能夠訪問供應(yīng)商資料。我們盡量保證及時(shí)更新資料；不過您可以從供應(yīng)商處了解最新資料。
2 一般屬性：這些不能被視為規(guī)格。
3 10°C/min
|