Celstran® PA66-GF20-02P11/12
聚酰胺66
Ticona
Technical Data
產(chǎn)品說(shuō)明
Nylon 66 reinforced by 20 weight percent long glass fibers. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long.
Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly.
The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding.
Can be used for substituting die cast metal with the advantage of Weight reduction, no corrosion problems, no post treatment.
總體
材料狀態(tài) • 已商用：當(dāng)前有效
資料 1 • Technical Datasheet (English)
• Processing - Injection (English)
Search for UL Yellow Card • Ticona
• Celstran®
供貨地區(qū) • 北美洲 • 歐洲
填料/增強(qiáng)材料 • 長(zhǎng)玻璃纖維, 20% 填料按重量
添加劑 • 熱穩(wěn)定劑
性能特點(diǎn) • 低翹曲性 • 高強(qiáng)度 • 熱穩(wěn)定性
• 剛性，高 • 耐低溫撞擊
用途 • 金屬置換
RoHS 合規(guī)性 • 聯(lián)系制造商
加工方法 • 注射成型
物理性能 額定值 單位制 測(cè)試方法
密度 1.30g/cm³ ISO 1183
機(jī)械性能 額定值 單位制 測(cè)試方法
拉伸模量
-- 8300MPa ISO 527-2/1A/1
80°C 4970MPa ISO 527-2
拉伸應(yīng)力
斷裂 125MPa ISO 527-2/1A/5
80°C 103MPa ISO 527-2
拉伸應(yīng)變
斷裂 1.6% ISO 527-2/1A/5
斷裂, 80°C 2.6% ISO 527-2
彎曲模量 ISO 178
23°C 7100MPa
80°C 4400MPa
彎曲強(qiáng)度 ISO 178
23°C 190MPa
80°C 175MPa
沖擊性能 額定值 單位制 測(cè)試方法
簡(jiǎn)支梁缺口沖擊強(qiáng)度 ISO 179/1eA
-30°C 27kJ/m²
23°C 24kJ/m²
簡(jiǎn)支梁缺口沖擊強(qiáng)度 ISO 179/1eU
-30°C 52kJ/m²
23°C 41kJ/m²
1 / 3
Celstran® PA66-GF20-02P11/12
聚酰胺66
Ticona
沖擊性能 額定值 單位制 測(cè)試方法
懸壁梁缺口沖擊強(qiáng)度 ISO 180/1A
-30°C 21kJ/m²
23°C 19kJ/m²
熱性能 額定值 單位制 測(cè)試方法
熱變形溫度
1.8 MPa, 未退火 260°C ISO 75-2/A
8.0 MPa, 未退火 238°C ISO 75-2/C
熔融溫度 3 260°C ISO 11357-3
備注
1 通過(guò)這些鏈接您能夠訪問(wèn)供應(yīng)商資料。我們盡量保證及時(shí)更新資料；不過(guò)您可以從供應(yīng)商處了解最新資料。
2 一般屬性：這些不能被視為規(guī)格。
3 10°C/min
|